冶金輔材
| 矽錳合金 | Mn: 65%min, Si: 14%min/ Mn: 65%min, Si: 16%min |
| Silico Manganese Alloy | |
| 輕燒鎂球 | 30~80mm |
| Light Burned Magnesia Ball | |
| 滑門砂 | SiO2: 35%min, Cr2O3: 27%max, Al2O3: 15%min |
| Ladle Filler Sand | |
| 橄欖砂 | MgO: 42%~46%, SiO2: 36%~40% |
| Raw Olivine Sand | |
螢石 |
CAF2: 95%, SiO2: 3.5%, CACO3: 0.8% CAF2: 90%, SiO2: 8%, CACO3: 1% CAF2: 80%, SiO2: 12%, CACO3: 3-6% CAF2: 75%, SiO2: 14%, CACO3: 4-6% SIZE: 0-5/5-30/30-70/10-30/10-70mm |
| Fluorspar Lump | |
| 焦碳(鍛燒無煙煤增碳劑) | FC: 90%min, Ash+VM: 10%max, Sulfur: 0.5%max, Moisture: 1%max |
| Carbon Additive | |
| 增碳劑 | FC: 98.5%min, H2O: 0.2max/ FC: 90%min, H2O: 1.0%max/ FC: 80%min, H2O: 0.2%max |
| Recarburizer | |
| 脫氧劑 | SiC: 40%min, Silicon: 10%min |
| Oxidation Material | |
| 脫磷劑 | Fe2O3: 25~35%min, CaO: 50~60%min |
| Dephosphorizing Agent | |
| 脫硫劑 | CaO: 60%min, CaF2: 10%max, Al2O3: 10%max |
| Desulfurizer | |
| 精煉渣 | CaO: 45%min, Al2O3: 35%min |
| Refined Slag | |
| 保溫覆蓋劑 | MgO: 85%min, CaO: 3%max |
| Tundish Powder | |
| 澆鑄粉 | SiO2: 27.1%min, CaO: 33.9%min |
| Casting Powder | |
| 鋁線 | 4mm+/-0.1mm , 1070, AL:99.7% min. |
| Aluminum Wire | |
鋁線 |
12mm 4mm+/-0.1mm .1060(軟態) AL:99.6%min,Si:0.25%max, Fe:0.35%max, Mg:0.03max,Cu:0.05% max, Zn:0.05%max,Mn:0.03% max,Ti:0.03%max,V:0.05% max |
| Aluminum Wire | |
| 矽鈣線 | Dia 13mm,OD 1300mm/ID 1200mm, Ø13mm±0.5mm, C: 1%max, Si:60 +/-5% max,P: 0.04% max, S: 0.06% max,CA: 28% min, AL:2.4% max |
| Silicon-calclum cored wire | |
| 純鈣線 | Dia 9mm OD 1100mm/ID 550mm,Ø9mm±0.5mm橫軸+內抽,密度: 70g/meter, Ca:98%min,Mg:1.0%max,Al:1.0% max,鋼皮: 0.6mm |
| Pure calcium cored wire |